Bicylindre de vis conique pour tuyau de pvc pour extrudeuse double
La spécification de conique deux hélices et le Canon
|
Specification
(d/D)
|
Work Length
(mm)
|
Extruding Ability
KG/H)
|
Screw Speed
(rmp)
|
Φ25/Φ53 |
540 |
25-40 |
5-50 |
Φ35/Ø77 |
810 |
40-70 |
5-50 |
Φ45/Φ90 |
990 |
50-80 |
5-45 |
Φ50/105 |
1070 |
100-150 |
4-45 |
Φ51/105 |
1220 |
100-150 |
4-40 |
Φ55/Φ110 |
1220 |
120-180 |
4-40 |
Φ60/Φ125 |
1320 |
150-200 |
4-40 |
Φ65/Φ120 |
1440 |
200-250 |
4-40 |
Φ65/Φ132 |
1440 |
200-250 |
4-40 |
Φ70/Φ140 |
1460 |
250-320 |
4-35 |
Φ75/Φ150 |
1480 |
300-360 |
4-35 |
Φ80/Φ143 |
1800 |
300-360 |
4-35 |
Φ80/Φ156 |
1660 |
300-360 |
4-35 |
Φ90/Φ184 |
2000 |
400-500 |
3-35 |
Technique Date (Description)
Material |
38 38CrMoALA,SKD61,D2 etc. |
Hardness After Hardening&Tempering |
HB260-290 |
Depth of Nitrided |
0.5-0.8mm |
Hardness of The Surface |
Hv950-1100 |
Surface Roughness |
Ra0.4um |
Linearity of Screw |
0.015mm/m |
Technique Date (en détail)
| Technical Parameter |
Base Material |
1)38CrMoAlA(JIS SACM645);2)Cr12MOV(JIS SKD-11) ;
3)4Cr5MoSiV1(JIS SKD-61) ;4)42CrMo(AISI 4140) |
| Bimetallic Alloy Materials |
1)Fe-based alloy 2)Ni-based alloy/Deloro alloy
3)Co-based alloy 4)NiCo-based alloy
5)Tungsten carbide/Wolfram carbide |
| Double-alloy level |
Level A - containing Tungsten of 40%
Level B - containing tungsten of 25%
Level C - containing tungsten of 15% |
| Surface Treatment |
Heat Treatment
High Frequency Treatment
Nitriding treatment(120 Hours):
Depth of Nitrided Layer: 0.5-0.8 mm
Hardness of Nitrided Layer: 900-1020Hv (HRC56°-65°)
Hard Chrome Plating treatment:
Thickness of Hard Chrome Plating Layer: 0.05-0.10mm
Hardness of Hard Chrome Plating Layer: ≥950HV
Nickel alloy plating.treatment:
Bimetallic Barrel/Cylinder: Centrifugal Casting (Inlay Alloy)
Bimetallic Screw: Plasma Alloy Coating Spraying
Depth of Bimetallic Layer: >2mm
Hardness of Bimetallic Layer: HRC55°-72°
Spraying corrosion wear-resisting dual metal layers
|
| Basic information |
Roughness of the surface:Ra0.4um
Linearity of the screw: ≤0.015mm
Linear axis limit: ≤0.02mm
Hardness after Hardening & Tempering: HB240-280
Fragility of Nitration:≤Two class
|
| Material Application |
1)General Plastics
2)ABS,PA,PC,PE,PET,PP,PS,EVA,PU,PVC,U-PVC,etc
3)PA + GF(Glass Fiber)
4)Flame-resistant Reinforced Plastics
5)Modified Engineering Plastics
6)All kinds of Mixed Recycled Material(in Scrap or Granule), PVC + 30% CaCo3, etc |
Vis conique de jumeau avec bimétalliques :
Deux barillets coniques :
Baril bimétallique :
Notre twin conique à vis et baril pourraient serive haute addtive de CaCo3 et de bois.
Le taux de compression de la canbe vis conçu selon les différents produits et mélanges.
Si vous avez n'importe quelle enquête, n'hésitez pas à nous en informer.
Baril vis conique jumeaux a été présenté ci-dessus, veulent plus similair, baril vis conique double cliquez.